Subjective and objective perceptions of specular gloss and surface roughness of esthetic resin composites before and after artificial aging


Barucci-Pfister, N; Göhring, T N (2009). Subjective and objective perceptions of specular gloss and surface roughness of esthetic resin composites before and after artificial aging. American Journal of Dentistry, 22(2):102-110.

Abstract

PURPOSE: To correlate measurements of specular gloss and surface roughness of resin composite materials with subjective perception of luster before and after artificial aging. METHODS: Polished specimens of eight composites were compared with human enamel (HE): microfilled SR Adoro (SR); microhybrid Artemis (AR), Enamel HFO (EHFO), Miris (MI), Tetric Ceram (TC), Venus (VE); and nanohybrid CeramX (CX) and nanofilled Filtek Supreme (FS). Before, during and after artificial aging (6000 thermal changes between 5 degrees C and 50 degrees C in an artificial oral environment, 240 hours storage in a container with ethanol, 300 minutes of toothbrushing), specular gloss and surface roughness were measured. Initial and endpoint gloss results were correlated with subjective luster rankings of 10 individuals. RESULTS: Artificial aging resulted in minor (EHFO, CX, FS), moderate (SR, MI, TC, VE) to high (AR) increases in surface roughness. Specular gloss decreased linearly for SR and FS, but decreased after an initial increase for all other materials. Subjectively, AR and FS were rated more and TC, VE and CX less lustrous than HE at baseline. After aging, luster of EHFO and FS was ranked higher and AR, TC, and VE lower than HE. Surface roughness was consistent with subjective perceptions (correlation coefficient: initial r = 0.913; endpoint r = 0.944, P < or = 0.0006), whereas specular gloss was consistent with subjective perceptions only after artificial aging (initial r = 0.616, P = 0.1084; endpoint r = 0.834, P = 0.0072).

PURPOSE: To correlate measurements of specular gloss and surface roughness of resin composite materials with subjective perception of luster before and after artificial aging. METHODS: Polished specimens of eight composites were compared with human enamel (HE): microfilled SR Adoro (SR); microhybrid Artemis (AR), Enamel HFO (EHFO), Miris (MI), Tetric Ceram (TC), Venus (VE); and nanohybrid CeramX (CX) and nanofilled Filtek Supreme (FS). Before, during and after artificial aging (6000 thermal changes between 5 degrees C and 50 degrees C in an artificial oral environment, 240 hours storage in a container with ethanol, 300 minutes of toothbrushing), specular gloss and surface roughness were measured. Initial and endpoint gloss results were correlated with subjective luster rankings of 10 individuals. RESULTS: Artificial aging resulted in minor (EHFO, CX, FS), moderate (SR, MI, TC, VE) to high (AR) increases in surface roughness. Specular gloss decreased linearly for SR and FS, but decreased after an initial increase for all other materials. Subjectively, AR and FS were rated more and TC, VE and CX less lustrous than HE at baseline. After aging, luster of EHFO and FS was ranked higher and AR, TC, and VE lower than HE. Surface roughness was consistent with subjective perceptions (correlation coefficient: initial r = 0.913; endpoint r = 0.944, P < or = 0.0006), whereas specular gloss was consistent with subjective perceptions only after artificial aging (initial r = 0.616, P = 0.1084; endpoint r = 0.834, P = 0.0072).

Citations

11 citations in Web of Science®
13 citations in Scopus®
Google Scholar™

Altmetrics

Downloads

3 downloads since deposited on 07 Dec 2009
0 downloads since 12 months
Detailed statistics

Additional indexing

Item Type:Journal Article, refereed, original work
Communities & Collections:04 Faculty of Medicine > Center for Dental Medicine > Clinic for Preventive Dentistry, Periodontology and Cariology
Dewey Decimal Classification:610 Medicine & health
Language:English
Date:April 2009
Deposited On:07 Dec 2009 11:15
Last Modified:05 Apr 2016 13:37
Publisher:Mosher & Linder
ISSN:0894-8275
Related URLs:https://www.zora.uzh.ch/23924/
PubMed ID:19626974
Permanent URL: https://doi.org/10.5167/uzh-25305

Download

[img]
Content: Accepted Version
Filetype: PDF - Registered users only
Size: 2MB

TrendTerms

TrendTerms displays relevant terms of the abstract of this publication and related documents on a map. The terms and their relations were extracted from ZORA using word statistics. Their timelines are taken from ZORA as well. The bubble size of a term is proportional to the number of documents where the term occurs. Red, orange, yellow and green colors are used for terms that occur in the current document; red indicates high interlinkedness of a term with other terms, orange, yellow and green decreasing interlinkedness. Blue is used for terms that have a relation with the terms in this document, but occur in other documents.
You can navigate and zoom the map. Mouse-hovering a term displays its timeline, clicking it yields the associated documents.

Author Collaborations