Bond strength of two resin cements on dentin using different cementation strategies


Melo, R M; Özcan, M; Barbosa, S H; Galhano, G; Amaral, R; Bottino, M A; Valandro, L F (2010). Bond strength of two resin cements on dentin using different cementation strategies. Journal of Esthetic and Restorative Dentistry, 22(4):262-268.

Abstract

PURPOSE: This study evaluated the microtensile bond strength of two resin cements to dentin either with their corresponding self-etching adhesives or employing the three-step "etch-and-rinse" technique. The null hypothesis was that the "etch-and-rinse" adhesive system would generate higher bond strengths than the self-etching adhesives.

MATERIALS AND METHODS: Thirty-two human molars were randomly divided into four groups (N = 32, n = 8/per group): G1) ED Primer self-etching adhesive + Panavia F; G2) All-Bond 2 "etch-and-rinse" adhesive + Panavia F; G3) Multilink primer A/B self-etching adhesive + Multilink resin cement; G4) All-Bond 2 + Multilink. After cementation of composite resin blocks (5 x 5 x 4 mm), the specimens were stored in water (37 degrees C, 24 hours), and sectioned to obtain beams (+/-1 mm(2) of adhesive area) to be submitted to microtensile test. The data were analyzed using 2-way analysis of variance and Tukey's test (alpha = 0.05).

RESULTS: Although the cement type did not significantly affect the results (p = 0.35), a significant effect of the adhesive system (p = 0.0001) was found on the bond strength results. Interaction terms were not significant (p = 0.88751). The "etch-and-rinse" adhesive provided significantly higher bond strength values (MPa) with both resin cements (G2: 34.4 +/- 10.6; G4: 33.0 +/- 8.9) compared to the self-etching adhesive systems (G1: 19.8 +/- 6.6; G3: 17.8 +/- 7.2) (p < 0.0001). Pretest failures were more frequent in the groups where self-etching systems were used.

CONCLUSION: Although the cement type did not affect the results, there was a significant effect of changing the bonding strategy. The use of the three-step "etch-and-rinse" adhesive resulted in significantly higher bond strength for both resin cements on dentin.

CLINICAL SIGNIFICANCE: Dual polymerized resin cements tested could deliver higher bond strength to dentin in combination with "etch-and-rinse" adhesive systems as opposed to their use in combination with self-etching adhesives.

PURPOSE: This study evaluated the microtensile bond strength of two resin cements to dentin either with their corresponding self-etching adhesives or employing the three-step "etch-and-rinse" technique. The null hypothesis was that the "etch-and-rinse" adhesive system would generate higher bond strengths than the self-etching adhesives.

MATERIALS AND METHODS: Thirty-two human molars were randomly divided into four groups (N = 32, n = 8/per group): G1) ED Primer self-etching adhesive + Panavia F; G2) All-Bond 2 "etch-and-rinse" adhesive + Panavia F; G3) Multilink primer A/B self-etching adhesive + Multilink resin cement; G4) All-Bond 2 + Multilink. After cementation of composite resin blocks (5 x 5 x 4 mm), the specimens were stored in water (37 degrees C, 24 hours), and sectioned to obtain beams (+/-1 mm(2) of adhesive area) to be submitted to microtensile test. The data were analyzed using 2-way analysis of variance and Tukey's test (alpha = 0.05).

RESULTS: Although the cement type did not significantly affect the results (p = 0.35), a significant effect of the adhesive system (p = 0.0001) was found on the bond strength results. Interaction terms were not significant (p = 0.88751). The "etch-and-rinse" adhesive provided significantly higher bond strength values (MPa) with both resin cements (G2: 34.4 +/- 10.6; G4: 33.0 +/- 8.9) compared to the self-etching adhesive systems (G1: 19.8 +/- 6.6; G3: 17.8 +/- 7.2) (p < 0.0001). Pretest failures were more frequent in the groups where self-etching systems were used.

CONCLUSION: Although the cement type did not affect the results, there was a significant effect of changing the bonding strategy. The use of the three-step "etch-and-rinse" adhesive resulted in significantly higher bond strength for both resin cements on dentin.

CLINICAL SIGNIFICANCE: Dual polymerized resin cements tested could deliver higher bond strength to dentin in combination with "etch-and-rinse" adhesive systems as opposed to their use in combination with self-etching adhesives.

Citations

4 citations in Web of Science®
4 citations in Scopus®
Google Scholar™

Altmetrics

Downloads

2 downloads since deposited on 06 Feb 2011
0 downloads since 12 months
Detailed statistics

Additional indexing

Item Type:Journal Article, refereed, original work
Communities & Collections:04 Faculty of Medicine > Center for Dental Medicine > Clinic for Fixed and Removable Prosthodontics
Dewey Decimal Classification:610 Medicine & health
Language:English
Date:2010
Deposited On:06 Feb 2011 11:09
Last Modified:05 Apr 2016 14:43
Publisher:Wiley-Blackwell
ISSN:1496-4155
Publisher DOI:https://doi.org/10.1111/j.1708-8240.2010.00349.x
PubMed ID:20690956
Permanent URL: https://doi.org/10.5167/uzh-44680

Download

[img]
Filetype: PDF (Verlags-PDF) - Registered users only
Size: 1MB
View at publisher

TrendTerms

TrendTerms displays relevant terms of the abstract of this publication and related documents on a map. The terms and their relations were extracted from ZORA using word statistics. Their timelines are taken from ZORA as well. The bubble size of a term is proportional to the number of documents where the term occurs. Red, orange, yellow and green colors are used for terms that occur in the current document; red indicates high interlinkedness of a term with other terms, orange, yellow and green decreasing interlinkedness. Blue is used for terms that have a relation with the terms in this document, but occur in other documents.
You can navigate and zoom the map. Mouse-hovering a term displays its timeline, clicking it yields the associated documents.

Author Collaborations