Effect of silica coating combined to a MDP-based primer on the resin bond to Y-TZP ceramic


May, L G; Passos, S P; Capelli, D B; Özcan, M; Bottino, M A; Valandro, L F (2010). Effect of silica coating combined to a MDP-based primer on the resin bond to Y-TZP ceramic. Journal of Biomedical Materials Research. Part B: Applied Biomaterials, 95(1):69-74.

Abstract

The aim of this study was to evaluate the influence of silica coating and 10-methacryloyloxydecyl dihydrogen phosphate (MDP)-based primer applications upon the bonding durability of a MDP-based resin cement to a yttrium stabilized tetragonal zirconia (Y-TZP) ceramic. Ninety-six Y-TZP tabs were embedded in an acrylic resin (free surface for adhesion: 5 × 5 mm(2)), ground finished and randomly divided into four groups (N = 24) according to the ceramic surface conditioning: (1) cleaning with isopropanol (ALC); (2) ALC + phosphoric acid etching + MDP-based primer application (MDP-primer); (3) silica coating + 3-methacryloyloxypropyl trimethoxysilane (MPS)-based coupling agent application (SiO2 + MPS-Sil); and (4) SiO2 + MDP-primer. The MDP-based resin cement was applied on the treated surface using a cylindrical mold (diameter= 3 mm). Half of the specimens from each surface conditioning were stored in distilled water (37 °C, 24 h) before testing. Another half of the specimens were stored (90 days) and thermo-cycled (12,000 x) during this period (90 d/TC) before testing. A shear bond strength (SBS) test was performed at a crosshead speed of 0.5 mm/min. Two factors composed the experimental design: ceramic conditioning strategy (in four levels) and storage condition (in two levels), totaling eight groups. After 90 d/TC (Tukey; p < 0.05), SiO2 + MDP-primer (24.40 MPa) promoted the highest SBS. The ALC and MDP-primer groups debonded spontaneously during 90 d/TC. Bonding values were higher and more stable in the SiO2 groups. The use of MDP-primer after silica coating increased the bond strength.

Abstract

The aim of this study was to evaluate the influence of silica coating and 10-methacryloyloxydecyl dihydrogen phosphate (MDP)-based primer applications upon the bonding durability of a MDP-based resin cement to a yttrium stabilized tetragonal zirconia (Y-TZP) ceramic. Ninety-six Y-TZP tabs were embedded in an acrylic resin (free surface for adhesion: 5 × 5 mm(2)), ground finished and randomly divided into four groups (N = 24) according to the ceramic surface conditioning: (1) cleaning with isopropanol (ALC); (2) ALC + phosphoric acid etching + MDP-based primer application (MDP-primer); (3) silica coating + 3-methacryloyloxypropyl trimethoxysilane (MPS)-based coupling agent application (SiO2 + MPS-Sil); and (4) SiO2 + MDP-primer. The MDP-based resin cement was applied on the treated surface using a cylindrical mold (diameter= 3 mm). Half of the specimens from each surface conditioning were stored in distilled water (37 °C, 24 h) before testing. Another half of the specimens were stored (90 days) and thermo-cycled (12,000 x) during this period (90 d/TC) before testing. A shear bond strength (SBS) test was performed at a crosshead speed of 0.5 mm/min. Two factors composed the experimental design: ceramic conditioning strategy (in four levels) and storage condition (in two levels), totaling eight groups. After 90 d/TC (Tukey; p < 0.05), SiO2 + MDP-primer (24.40 MPa) promoted the highest SBS. The ALC and MDP-primer groups debonded spontaneously during 90 d/TC. Bonding values were higher and more stable in the SiO2 groups. The use of MDP-primer after silica coating increased the bond strength.

Citations

31 citations in Web of Science®
32 citations in Scopus®
Google Scholar™

Altmetrics

Downloads

2 downloads since deposited on 06 Feb 2011
0 downloads since 12 months
Detailed statistics

Additional indexing

Item Type:Journal Article, refereed, original work
Communities & Collections:04 Faculty of Medicine > Center for Dental Medicine > Clinic for Fixed and Removable Prosthodontics
Dewey Decimal Classification:610 Medicine & health
Language:English
Date:2010
Deposited On:06 Feb 2011 11:03
Last Modified:05 Apr 2016 14:43
Publisher:Wiley-Blackwell
ISSN:1552-4973
Publisher DOI:https://doi.org/10.1002/jbm.b.31684
PubMed ID:20690176

Download

[img]
Filetype: PDF (Verlags-PDF) - Registered users only
Size: 1MB
View at publisher

TrendTerms

TrendTerms displays relevant terms of the abstract of this publication and related documents on a map. The terms and their relations were extracted from ZORA using word statistics. Their timelines are taken from ZORA as well. The bubble size of a term is proportional to the number of documents where the term occurs. Red, orange, yellow and green colors are used for terms that occur in the current document; red indicates high interlinkedness of a term with other terms, orange, yellow and green decreasing interlinkedness. Blue is used for terms that have a relation with the terms in this document, but occur in other documents.
You can navigate and zoom the map. Mouse-hovering a term displays its timeline, clicking it yields the associated documents.

Author Collaborations