Effects of de- and remineralization of dentin on bond strengths yielded by one-, three-, and four-step adhesives


Schmidlin, P R; Siebenmann, J; Kocher, P; Seemann, R; Attin, T; Bindl, A (2008). Effects of de- and remineralization of dentin on bond strengths yielded by one-, three-, and four-step adhesives. Journal of Adhesive Dentistry, 10(2):119-126.

Abstract

PURPOSE: To assess the effect of different peri- and intertubular dentin mineralization conditions and etching on shear bond strength in vitro. MATERIALS AND METHODS: One hundred fifty crowns of extracted bovine incisors were embedded in resin and ground to expose the buccal coronal dentin. Sixty specimens were subjected to a demineralizing solution (DS) and another 60 teeth to a bacterial-based laboratory caries model (S. mutans, SM). Thirty specimens of each demineralization protocol (DS and SM) were randomly selected and remineralized (-R). Thirty sound dentin specimens served as control (C). Resin composite buildups (Tetric) were bonded after application of one of the following adhesives: a one-step self-etching adhesive (Xeno III), and a self-etching adhesive (Syntac Classic) without (three-step) and with prior additional 35% phosphoric acid etching (etch-and-rinse, four-step). Teeth were subjected to shear bond strength testing in a universal testing device at a crosshead speed of 0.5 mm/min (Ultradent method). RESULTS: Bond strength value for group C ranged from 6.3 to 8.4 MPa (p > 0.05). DS and DS-R samples showed in creased bond strength with the one-step adhesive (11.6 MPa, p < 0.05), whereas the three-step adhesive with additional etching showed decreased bond strength (3.2 MPa, p < 0.05). SM samples showed the lowest bond strength of all adhesive systems (range 1.1 to 1.5 MPa, p > 0.05). Remineralization showed no effect on the latter group. CONCLUSION: The degree of mineralization of the dentin is important for adhesion. Additional etching with phosphori acid reduced bond strength of a three-step adhesive.

PURPOSE: To assess the effect of different peri- and intertubular dentin mineralization conditions and etching on shear bond strength in vitro. MATERIALS AND METHODS: One hundred fifty crowns of extracted bovine incisors were embedded in resin and ground to expose the buccal coronal dentin. Sixty specimens were subjected to a demineralizing solution (DS) and another 60 teeth to a bacterial-based laboratory caries model (S. mutans, SM). Thirty specimens of each demineralization protocol (DS and SM) were randomly selected and remineralized (-R). Thirty sound dentin specimens served as control (C). Resin composite buildups (Tetric) were bonded after application of one of the following adhesives: a one-step self-etching adhesive (Xeno III), and a self-etching adhesive (Syntac Classic) without (three-step) and with prior additional 35% phosphoric acid etching (etch-and-rinse, four-step). Teeth were subjected to shear bond strength testing in a universal testing device at a crosshead speed of 0.5 mm/min (Ultradent method). RESULTS: Bond strength value for group C ranged from 6.3 to 8.4 MPa (p > 0.05). DS and DS-R samples showed in creased bond strength with the one-step adhesive (11.6 MPa, p < 0.05), whereas the three-step adhesive with additional etching showed decreased bond strength (3.2 MPa, p < 0.05). SM samples showed the lowest bond strength of all adhesive systems (range 1.1 to 1.5 MPa, p > 0.05). Remineralization showed no effect on the latter group. CONCLUSION: The degree of mineralization of the dentin is important for adhesion. Additional etching with phosphori acid reduced bond strength of a three-step adhesive.

Citations

6 citations in Web of Science®
7 citations in Scopus®
Google Scholar™

Downloads

2 downloads since deposited on 07 Nov 2008
0 downloads since 12 months
Detailed statistics

Additional indexing

Item Type:Journal Article, refereed, original work
Communities & Collections:04 Faculty of Medicine > Center for Dental Medicine > Clinic for Preventive Dentistry, Periodontology and Cariology
Dewey Decimal Classification:610 Medicine & health
Language:English
Date:February 2008
Deposited On:07 Nov 2008 08:00
Last Modified:05 Apr 2016 12:31
Publisher:Quintessence Publishing
ISSN:1461-5185
PubMed ID:18512509
Permanent URL: http://doi.org/10.5167/uzh-4737

Download

[img]
Content: Accepted Version
Filetype: PDF - Repository staff only
Size: 6MB

TrendTerms

TrendTerms displays relevant terms of the abstract of this publication and related documents on a map. The terms and their relations were extracted from ZORA using word statistics. Their timelines are taken from ZORA as well. The bubble size of a term is proportional to the number of documents where the term occurs. Red, orange, yellow and green colors are used for terms that occur in the current document; red indicates high interlinkedness of a term with other terms, orange, yellow and green decreasing interlinkedness. Blue is used for terms that have a relation with the terms in this document, but occur in other documents.
You can navigate and zoom the map. Mouse-hovering a term displays its timeline, clicking it yields the associated documents.

Author Collaborations