Durability and Weibull Characteristics of Lithium Disilicate Crowns Bonded on Abutments with Knife-Edge and Large Chamfer Finish Lines after Cyclic Loading


Cortellini, Davide; Canale, Angelo; Souza, Rodrigo O A; Campos, Fernanda; Lima, Julia C; Özcan, Mutlu (2015). Durability and Weibull Characteristics of Lithium Disilicate Crowns Bonded on Abutments with Knife-Edge and Large Chamfer Finish Lines after Cyclic Loading. Journal of Prosthodontics, 24(8):615-619.

Abstract

PURPOSE The aim of this study was to evaluate the durability of lithium disilicate crowns bonded on abutments prepared with two types of finish lines after long-term cyclic loading. MATERIALS AND METHODS Pressed lithium disilicate all-ceramic molar crowns were bonded (Variolink II) to epoxy abutments (height: 5.5 mm, Ø: 7.5 mm, conicity: 6°) (N = 20) with either knife-edge (KE) or large chamfer (LC) finish lines. Each assembly was submitted to cyclic loading (1,200,000×; 200 N; 1 Hz) in water and then tested until fracture in a universal testing machine (1 mm/min). Failure types were classified and further evaluated under stereomicroscope and SEM. The data (N) were analyzed using one-way ANOVA. Weibull distribution values including the Weibull modulus (m), characteristic strength (0), probability of failure at 5% (0.05), 1% (0.01), and correlation coefficient were calculated. RESULTS Type of finish line did not significantly influence the mean fracture strength of pressed ceramic crowns (KE: 1655 ± 353 N; LC: 1618 ± 263 N) (p = 0.7898). Weibull distribution presented lower shape value (m) of KE (m = 5.48; CI: 3.5 to 8.6) compared to LC (m = 7.68; CI: 5.2 to 11.3). Characteristic strengths (0) (KE: 1784.9 N; LC: 1712.1 N) were higher than probability of failure at 5% (0.05) (KE: 1038.1 N; LC: 1163.4 N) followed by 1% (0.01) (KE: 771 N; LC: 941.1 N), with a correlation coefficient of 0.966 for KE and 0.924 for LC. Type V failures (severe fracture of the crown and/or tooth) were more common in both groups. SEM findings showed that fractures occurred mainly from the cement/ceramic interface at the occlusal side of the crowns. CONCLUSION Lithium disilicate ceramic crowns bonded onto abutment teeth with KE preparation resulted in similar fracture strength to those bonded on abutments with LC finish line. CLINICAL SIGNIFICANCE Pressed lithium disilicate ceramic crowns may not require invasive finish line preparations since finish line type did not impair the strength after aging conditions.

Abstract

PURPOSE The aim of this study was to evaluate the durability of lithium disilicate crowns bonded on abutments prepared with two types of finish lines after long-term cyclic loading. MATERIALS AND METHODS Pressed lithium disilicate all-ceramic molar crowns were bonded (Variolink II) to epoxy abutments (height: 5.5 mm, Ø: 7.5 mm, conicity: 6°) (N = 20) with either knife-edge (KE) or large chamfer (LC) finish lines. Each assembly was submitted to cyclic loading (1,200,000×; 200 N; 1 Hz) in water and then tested until fracture in a universal testing machine (1 mm/min). Failure types were classified and further evaluated under stereomicroscope and SEM. The data (N) were analyzed using one-way ANOVA. Weibull distribution values including the Weibull modulus (m), characteristic strength (0), probability of failure at 5% (0.05), 1% (0.01), and correlation coefficient were calculated. RESULTS Type of finish line did not significantly influence the mean fracture strength of pressed ceramic crowns (KE: 1655 ± 353 N; LC: 1618 ± 263 N) (p = 0.7898). Weibull distribution presented lower shape value (m) of KE (m = 5.48; CI: 3.5 to 8.6) compared to LC (m = 7.68; CI: 5.2 to 11.3). Characteristic strengths (0) (KE: 1784.9 N; LC: 1712.1 N) were higher than probability of failure at 5% (0.05) (KE: 1038.1 N; LC: 1163.4 N) followed by 1% (0.01) (KE: 771 N; LC: 941.1 N), with a correlation coefficient of 0.966 for KE and 0.924 for LC. Type V failures (severe fracture of the crown and/or tooth) were more common in both groups. SEM findings showed that fractures occurred mainly from the cement/ceramic interface at the occlusal side of the crowns. CONCLUSION Lithium disilicate ceramic crowns bonded onto abutment teeth with KE preparation resulted in similar fracture strength to those bonded on abutments with LC finish line. CLINICAL SIGNIFICANCE Pressed lithium disilicate ceramic crowns may not require invasive finish line preparations since finish line type did not impair the strength after aging conditions.

Statistics

Citations

2 citations in Web of Science®
2 citations in Scopus®
Google Scholar™

Altmetrics

Downloads

2 downloads since deposited on 10 Dec 2015
0 downloads since 12 months
Detailed statistics

Additional indexing

Item Type:Journal Article, refereed, original work
Communities & Collections:04 Faculty of Medicine > Center for Dental Medicine > Clinic for Fixed and Removable Prosthodontics
Dewey Decimal Classification:610 Medicine & health
Language:English
Date:2015
Deposited On:10 Dec 2015 13:19
Last Modified:22 Jan 2017 06:33
Publisher:Wiley-Blackwell Publishing, Inc.
ISSN:1059-941X
Publisher DOI:https://doi.org/10.1111/jopr.12237
PubMed ID:25319113

Download