Schmelz-Fluoridaufnahme nach Fluoridierung und Fluoridfällung


Buchalla, W; Lennon, A M; Trage, K; Becker, K; Attin, T (2007). Schmelz-Fluoridaufnahme nach Fluoridierung und Fluoridfällung. Schweizer Monatsschrift für Zahnmedizin SMfZ, 117(2):118-122.

Abstract

This study is on fluoride uptake into enamel following fluoride precipitation with calcium hydroxide. Five specimens each from 12 bovine incisors were polished, covered with a salivary pellicle, and distributed into five groups (n=12). A fluoride solution (43,500 ppm F from magnesiumfluorosilicate, copper-(II)-fluorosilicate and sodium-fluoride, pH 2; Tiefenfluorid Touchierlösung, Humanchemie) and Ca(OH)2-solution (Tiefenfluorid Nachtouchierlösung) were applied subsequently in group TN. "Touchierlosung" only was used in group T, sodium-fluoride (43,500 ppm F, pH 2) in group NaF, and aminefluoride (Elmex fluid, 10,000 ppm F, pH 4) in group EF. No fluoride was used in group NK (negative control). Following rinsing and 24 h storage in artificial saliva surface KOH-soluble fluoride content (KOHF), and structurally bound fluoride content (SBF) from three layers (0-33, 33-66 and 66-99 pm) was determined by fluoride electrode procedures. KOHF (median in microg/cm2) of NK was below the lower limit of quantification of the fluoride electrode. The other group values were significantly higher (Mann-Whitney test, p < or = 0.05). TN (1.6), T (1.4) and NaF (1.1) did not differ significantly. EF (0.6) was significantly smaller than TN and T but not smaller than NaF. SBF (0-33, 33-66, 66-99 pm; median in microg/cm3) of TN (445, 341, 275), T (644, 481, 360), NaF (804, 480, 307) and EF (449, 346, 280) did not differ significantly but, with the exception of TN, were significantly higher as compared to NK. A precipitation reaction with Ca(OH)2 following fluoridation did not increase enamel fluoride uptake.

Abstract

This study is on fluoride uptake into enamel following fluoride precipitation with calcium hydroxide. Five specimens each from 12 bovine incisors were polished, covered with a salivary pellicle, and distributed into five groups (n=12). A fluoride solution (43,500 ppm F from magnesiumfluorosilicate, copper-(II)-fluorosilicate and sodium-fluoride, pH 2; Tiefenfluorid Touchierlösung, Humanchemie) and Ca(OH)2-solution (Tiefenfluorid Nachtouchierlösung) were applied subsequently in group TN. "Touchierlosung" only was used in group T, sodium-fluoride (43,500 ppm F, pH 2) in group NaF, and aminefluoride (Elmex fluid, 10,000 ppm F, pH 4) in group EF. No fluoride was used in group NK (negative control). Following rinsing and 24 h storage in artificial saliva surface KOH-soluble fluoride content (KOHF), and structurally bound fluoride content (SBF) from three layers (0-33, 33-66 and 66-99 pm) was determined by fluoride electrode procedures. KOHF (median in microg/cm2) of NK was below the lower limit of quantification of the fluoride electrode. The other group values were significantly higher (Mann-Whitney test, p < or = 0.05). TN (1.6), T (1.4) and NaF (1.1) did not differ significantly. EF (0.6) was significantly smaller than TN and T but not smaller than NaF. SBF (0-33, 33-66, 66-99 pm; median in microg/cm3) of TN (445, 341, 275), T (644, 481, 360), NaF (804, 480, 307) and EF (449, 346, 280) did not differ significantly but, with the exception of TN, were significantly higher as compared to NK. A precipitation reaction with Ca(OH)2 following fluoridation did not increase enamel fluoride uptake.

Statistics

Citations

Altmetrics

Downloads

210 downloads since deposited on 16 Jun 2008
17 downloads since 12 months
Detailed statistics

Additional indexing

Other titles:Enamel fluoride uptake following fluoride application and fluoride precipitation
Item Type:Journal Article, refereed, original work
Communities & Collections:04 Faculty of Medicine > Center for Dental Medicine > Clinic for Preventive Dentistry, Periodontology and Cariology
Dewey Decimal Classification:610 Medicine & health
Language:German
Date:February 2007
Deposited On:16 Jun 2008 14:38
Last Modified:05 Apr 2016 12:23
Publisher:Schweizerische Zahnärzte-Gesellschft
ISSN:0256-2855
Additional Information:Free full text article
Official URL:http://www.sso.ch/doc/doc_download.cfm?uuid=95653B42D9D9424C45F60F191944E384&&IRACER_AUTOLINK&&
PubMed ID:17345998

Download

Download PDF  'Schmelz-Fluoridaufnahme nach Fluoridierung und Fluoridfällung'.
Preview
Filetype: PDF
Size: 1MB