Effect of caries infiltrant application on shear bond strength of different adhesive systems to sound and demineralized enamel


Jia, Liuhe; Stawarczyk, Bogna; Schmidlin, Patrick R; Attin, Thomas; Wiegand, Annette (2012). Effect of caries infiltrant application on shear bond strength of different adhesive systems to sound and demineralized enamel. Journal of Adhesive Dentistry, 14(6):569-574.

Abstract

Purpose: To investigate the influence of caries infiltrant application on the shear bond strength of different adhesives on sound and demineralized enamel. Materials and Methods: Sound and artificially demineralized (14 days, acidic buffer, pH 5.0) bovine enamel specimens were treated with a caries infiltrant (Icon, DMG), three different commercial adhesives (unfilled etchand- rinse adhesive: Heliobond, Ivoclar Vivadent; filled etch-and-rinse adhesive: Optibond FL, Kerr; or self-etching adhesive: iBOND Self Etch, Heraeus Kulzer) or a combination of caries infiltrant and adhesive. The shear bond strength of a nanohybrid composite was analyzed after thermocycling (5000x, 5° to 55°C) at a crosshead speed of 1 mm/min. Failure mode was inspected under a stereomicroscope at 25X magnification. Results: In both sound and demineralized enamel, the shear bond strength of the caries infiltrant was not significantly different from the etch-and-rinse adhesives, while the self-etching adhesive showed significantly lower values compared to all other groups. Pretreatment with the caries infiltrant significantly increased the bond strength of the self-etching adhesive in both substrates and of the filled etch-and-rinse adhesive in demineralized enamel. While shear bond strength was not significantly different between the two substrates, cohesive failures were more likely to occur in demineralized than sound specimens. Conclusion: The shear bond strength of the caries infiltrant was similar to the etch-and-rinse adhesives. The caries infiltrant did not impair bonding to sound or demineralized enamel, and even increased adhesion of the selfetching agent.

Abstract

Purpose: To investigate the influence of caries infiltrant application on the shear bond strength of different adhesives on sound and demineralized enamel. Materials and Methods: Sound and artificially demineralized (14 days, acidic buffer, pH 5.0) bovine enamel specimens were treated with a caries infiltrant (Icon, DMG), three different commercial adhesives (unfilled etchand- rinse adhesive: Heliobond, Ivoclar Vivadent; filled etch-and-rinse adhesive: Optibond FL, Kerr; or self-etching adhesive: iBOND Self Etch, Heraeus Kulzer) or a combination of caries infiltrant and adhesive. The shear bond strength of a nanohybrid composite was analyzed after thermocycling (5000x, 5° to 55°C) at a crosshead speed of 1 mm/min. Failure mode was inspected under a stereomicroscope at 25X magnification. Results: In both sound and demineralized enamel, the shear bond strength of the caries infiltrant was not significantly different from the etch-and-rinse adhesives, while the self-etching adhesive showed significantly lower values compared to all other groups. Pretreatment with the caries infiltrant significantly increased the bond strength of the self-etching adhesive in both substrates and of the filled etch-and-rinse adhesive in demineralized enamel. While shear bond strength was not significantly different between the two substrates, cohesive failures were more likely to occur in demineralized than sound specimens. Conclusion: The shear bond strength of the caries infiltrant was similar to the etch-and-rinse adhesives. The caries infiltrant did not impair bonding to sound or demineralized enamel, and even increased adhesion of the selfetching agent.

Statistics

Citations

Dimensions.ai Metrics
11 citations in Web of Science®
14 citations in Scopus®
12 citations in Microsoft Academic
Google Scholar™

Altmetrics

Downloads

161 downloads since deposited on 28 Jan 2013
31 downloads since 12 months
Detailed statistics

Additional indexing

Item Type:Journal Article, refereed, original work
Communities & Collections:04 Faculty of Medicine > Center for Dental Medicine > Clinic for Preventive Dentistry, Periodontology and Cariology
04 Faculty of Medicine > Center for Dental Medicine > Clinic for Fixed and Removable Prosthodontics
Dewey Decimal Classification:610 Medicine & health
Language:English
Date:2012
Deposited On:28 Jan 2013 07:57
Last Modified:17 Feb 2018 00:43
Publisher:Quintessence Publishing
ISSN:1461-5185
OA Status:Green
Publisher DOI:https://doi.org/10.3290/j.jad.a25685
PubMed ID:22724105

Download

Download PDF  'Effect of caries infiltrant application on shear bond strength of different adhesive systems to sound and demineralized enamel'.
Preview
Content: Accepted Version
Filetype: PDF
Size: 172kB
View at publisher