Effect of surface conditioning methods on the microtensile bond strength of repair composite to indirect restorative materials


Mumcu, Emre; Erdemir, Ugur; Özsoy, Alev; Tekbas-Atay, Meltem; Özcan, Mutlu (2019). Effect of surface conditioning methods on the microtensile bond strength of repair composite to indirect restorative materials. Journal of Adhesion Science and Technology, 33(21):2369-2384.

Abstract

This study evaluated the effect of surface conditioning methods on the microtensile bond strength (µTBS) of a restorative composite to indirect restorative materials. Blocks (5 × 5 × 4 mm3) (N = 72) of (a) Zirconia (In-Ceram Zirconia, Vita) (ZR), (b) lithium disilicate glass ceramic (IPS Empress II, Ivoclar Vivadent) (LD), (c) Indirect resin composite (Gradia, GC) (GR) were fabricated (n = 24 per group) and divided randomly into three groups: 1-Control: no conditioning, 2-Silane coupling agent, 3-Hydrofluoric acid (9.5%) (HF)+silane. Each block was duplicated in resin composite. The adhesion surfaces were conditioned with airborne-particle abrasion (110 µm Al2O3 particles). Half of the conditioned blocks received no bonding and the other half one coat of bonding (ED Primer II, Kuraray). Each conditioned block was bonded to a composite block with a resin luting agent (Panavia F2.0, Kuraray). The blocks were sectioned into 1 mm2 microsticks and tested for microtensile bond strength (µTBS) (0.5 mm/min) in a μTBS testing machine. Failure types were evaluated under stereomicroscope and Scanning Electron Microscope (SEM). Data were analyzed using three-way ANOVA, Bonferroni corrected and independent sample t-tests (p < 0.05). Significant effect of the bonding (p < 0.001) and surface conditioning (p < 0.001) were observed in all groups. The highest mean bond strength values were obtained in the bonded, HF etched and silanized groups of ZR, LD and GR (12.4 ± 2.9, 28.1 ± 1.5 and 27.2 ± 2 MPa, respectively). HF acid + silane increased the repair bond values in all materials. Majority of the failure types were adhesive for ZR group, whereas HF + silane conditioned LD and GR groups presented predominantly cohesive failures in the cement.

Abstract

This study evaluated the effect of surface conditioning methods on the microtensile bond strength (µTBS) of a restorative composite to indirect restorative materials. Blocks (5 × 5 × 4 mm3) (N = 72) of (a) Zirconia (In-Ceram Zirconia, Vita) (ZR), (b) lithium disilicate glass ceramic (IPS Empress II, Ivoclar Vivadent) (LD), (c) Indirect resin composite (Gradia, GC) (GR) were fabricated (n = 24 per group) and divided randomly into three groups: 1-Control: no conditioning, 2-Silane coupling agent, 3-Hydrofluoric acid (9.5%) (HF)+silane. Each block was duplicated in resin composite. The adhesion surfaces were conditioned with airborne-particle abrasion (110 µm Al2O3 particles). Half of the conditioned blocks received no bonding and the other half one coat of bonding (ED Primer II, Kuraray). Each conditioned block was bonded to a composite block with a resin luting agent (Panavia F2.0, Kuraray). The blocks were sectioned into 1 mm2 microsticks and tested for microtensile bond strength (µTBS) (0.5 mm/min) in a μTBS testing machine. Failure types were evaluated under stereomicroscope and Scanning Electron Microscope (SEM). Data were analyzed using three-way ANOVA, Bonferroni corrected and independent sample t-tests (p < 0.05). Significant effect of the bonding (p < 0.001) and surface conditioning (p < 0.001) were observed in all groups. The highest mean bond strength values were obtained in the bonded, HF etched and silanized groups of ZR, LD and GR (12.4 ± 2.9, 28.1 ± 1.5 and 27.2 ± 2 MPa, respectively). HF acid + silane increased the repair bond values in all materials. Majority of the failure types were adhesive for ZR group, whereas HF + silane conditioned LD and GR groups presented predominantly cohesive failures in the cement.

Statistics

Citations

Dimensions.ai Metrics
1 citation in Web of Science®
1 citation in Scopus®
Google Scholar™

Altmetrics

Downloads

12 downloads since deposited on 07 Feb 2020
10 downloads since 12 months
Detailed statistics

Additional indexing

Item Type:Journal Article, refereed, original work
Communities & Collections:04 Faculty of Medicine > Center for Dental Medicine > Clinic of Reconstructive Dentistry
Dewey Decimal Classification:610 Medicine & health
Scopus Subject Areas:Physical Sciences > General Chemistry
Physical Sciences > Mechanics of Materials
Physical Sciences > Surfaces and Interfaces
Physical Sciences > Surfaces, Coatings and Films
Physical Sciences > Materials Chemistry
Uncontrolled Keywords:Materials Chemistry, Mechanics of Materials, General Chemistry, Surfaces, Coatings and Films, Surfaces and Interfaces
Language:English
Date:2 November 2019
Deposited On:07 Feb 2020 14:12
Last Modified:29 Jul 2020 13:57
Publisher:Taylor & Francis
ISSN:0169-4243
Additional Information:This is an Accepted Manuscript of an article published by Taylor & Francis in Journal of Adhesion Science and Technology on 17 Jul 2019 available online: http://wwww.tandfonline.com/https://doi.org/10.1080/01694243.2019.1640173
OA Status:Green
Publisher DOI:https://doi.org/10.1080/01694243.2019.1640173

Download

Green Open Access

Download PDF  'Effect of surface conditioning methods on the microtensile bond strength of repair composite to indirect restorative materials'.
Preview
Content: Accepted Version
Language: English
Filetype: PDF
Size: 507kB
View at publisher